This film is a clear film with Low Haze used specially for Reprographics, Labels, OHP and Photosensitive coating In this clear film is also used in Packaging for Window Lamination.
Sr.No
Property
Unit
Test Method
Typical Values
- General
-
-
-
-
-
-
-
-
-
1 Thickness
Micron
Polymers
25
36
50
75
100
125
175
2 Yield
M2/Kg
Polymers
31
19.8
14.3
9.5
7.14
5.71
4.0
3 Density
gm/cc
ASTM-D-1505
1.4
1.4
1.4
1.4
1.4
1.4
1.4
- Mechanical
-
-
-
-
-
-
-
-
-
1 Tensile Strength
at break (MD/TD)
Kg/cm2
ASTM-D-882
2000
1800
1800
1900
1800
1800
1700
2 Elongation (MD/TD)
%
ASTM-D-882
100
130
130
120
130
130
130
3 Slip (COF)
-
ASTM-D-1894
0.4
0.4
0.4
0.4
0.4
0.4
0.4
- Optical
-
-
-
-
-
-
-
-
-
1 Haze
%
ASTM-D-1003
1.5
1.5
1.5
1.5
1.5
1.5
2
2 Total Luminous Transmission
%
ASTM-D-1003
89
89
89
89
89
89
89
- Colour Values
-
-
-
-
-
-
-
-
-
1 L (Min)
-
CILAB (SCALE)
89.5
89.5
89.5
89.5
89.5
89.5
89.5
2 a (Max)
-
By Hunter Lab
Colour spectro-
photometer
0.4
 1.5
0.4
 1.5
0.4
 1.5
0.4
 1.5
0.4
1.5
0.4
 1.5
0.4
1.5
3 b (Max)
--
- Thermal
-
-
-
-
-
-
-
-
-
1 Shrinkage @150°C 30 min
MD
TD


%
%
ASTM-D-1204

 


1.1
0.5


1.1
0.5


1.1
0.5


1.1
0.5


1.1
0.5


1.1
0.5


1.1
0.5
2 Melting Point
°C

DSC
255
255
255
255
255
255
255
3 Coeff of Thermal Expansion
between 20°C& 50°C
1/K
(cm/cm/°C)
-
19 X 10 -6 (MD)
16 X 10 -6 (TD)
- Roll
1 Roll Width - Max
MM
Polymers
1600
1600
1600
1600
1600
1600
1550
2 Standard Length - Min
Mtrs
Polymers
1650
1050
750
500
375
300
225
3 Standard Length - Max

Mtrs
Polymers
6600
4200
4500
3000
2500
1800
1200

MD - Machine Direction
TD - Transverse Direction

Roll - ID / OD / Length / Width - Available as per customers specifications

The data given above has been obtained using standard test procedures on defined specimens. The results
should therefore only be regarded as a general guide to material properties and not as design data