| Polyester/BOPP Film is mainly used to manufacture Pressure Sensitive Tapes, in which adhesive coating is being applied on the top of the Film to produce Adhesive Tapes & Lable Stocks. This Adhesive tape has wide application in Packaging & Electrical Insulation Industries. Whilst, in Lable Stock Industries, Polyester Film is also used for shampoo Lables, Oil Lables, Bar coding etc.White Opaque Film (50 MIC) is mainly used in Pressure Sensitive Lables & General printing applications. | |||||||||||
|
Sr.
Nos |
Property
|
Unit
|
Test
Method
|
Typical
Values
|
|||||||
| - | General |
-- | -- | -- | -- | -- |
Polyester
Film
|
--
|
--
|
BOPP Film
|
--
|
|
1
|
Thickness
|
Micron
|
Polymers |
Clear
25 |
Metallised
25 |
Clear
36 |
Clear
50 |
WhiteOpq
50 |
Matt
50 |
TA
25 TI
25 |
TA
30 TI
30 |
|
2
|
Yield
|
M2/Kg
|
Polymers |
31
|
29.4
|
19.8
|
14.3
|
14.3
|
14.3
|
43.95
|
37
|
|
3
|
Density
|
gm/cc
|
ASTM-D-1505 |
1.4
|
2
to 2.3
|
1.4
|
1.4
|
1.45
|
1.4
|
0.9
|
0.9
|
|
-
|
Mechanical
|
--
|
-- |
--
|
--
|
--
|
--
|
--
|
--
|
--
|
--
|
|
1
|
Tensile
Strength at break (MD/TD)
|
Kg/cm2
|
ASTM-D-882 |
2000
|
1800
|
2000
|
2000
|
1550
|
1800
|
1300-2500
|
1300-2500
|
|
2
|
Elongation
(MD/TD)
|
%
|
ASTM-D-882 |
100
|
100
|
100
|
130
|
100
|
130
|
150-50
|
150-50
|
|
3
|
Slip
(COF)
|
-
|
ASTM-D-1894 |
0.5
|
-
|
0.4
|
0.4
|
0.4
|
0.3
|
0.35
|
0.35
|
|
-
|
Optical
|
-
|
- |
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
|
1
|
Haze
|
%
|
ASTM-D-1003 |
5
|
-
|
8
|
10
|
-
|
72
|
2.5
|
2.5
|
|
2
|
Gloss
at 45°C
|
%
|
ASTM-D-2457 |
-
|
-
|
-
|
- |
35
|
65
|
90
|
90
|
|
3
|
Total
luminous transmission
|
_
|
ASTM-D-2457 |
86
|
-
|
-
|
- |
-
|
76
|
-
|
-
|
|
4
|
VLT
|
%
|
ASTM-D-1003 |
-
|
-
|
-
|
- |
15
|
-
|
-
|
-
|
|
-
|
Thermal
|
-
|
- |
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
|
1
|
Shrinkage
@150°C 30 min
MD TD |
%
% |
ASTM-D-1204 |
3
1 |
2.0
2.0 |
1.6
0.4 |
1.2
0.4 |
2.6
0.4 |
1.6
0.4 |
4.0
2.0 |
4.0
2.0 |
|
|
|||||||||||
| MD
- Machine Direction TD - Transverse Direction Roll - ID / OD / Length / Width - Available as per customers specifications The data given above has been obtained using standard test procedures on defined specimens. The results should therefore only be regarded as a general guide to material properties and not as design data |
|||||||||||